Abstract Aluminium casting alloy LM4 (EN 1706 AC-45200) composites with TiB2 (1, 2, and 3 wt.%) as reinforcements were produced using the two-stage stir casting method. OM and SEM study shows uniform and homogeneous reinforcement distribution in LM4 + TiB2 composites. As-cast composites were subjected to single-stage solution treatment at 520°C for 2 h and multistage solution treatment at 495 and 520°C for 2 and 4 h, followed by hot water quenching at 60°C and aging at 100 and 200°C for different time intervals. The hardness of as-cast and artificially aged composites were compared in both conditions. Compared to as-cast LM4 alloy, 20-45% improvement in hardness was observed for LM4 + TiB2 as-cast composites. 60-150% improvement in hardness was observed in artificially aged LM4 + 3 wt.% TiB2 composites when aged at 100 and 200°C during peak aged conditions. TEM images confirmed the presence of primary strengthening solute-rich phases after age hardening treatment such as θ’-Al2Cu and θ”-Al3Cu, which are responsible for hardness increment. An artificial neural network (ANN) model was created to predict the hardness trend of these composite samples using MATLAB R2021b, and results proved that the ANN model developed can be utilized as an effective tool to predict the hardness of treated composite samples.

The present work is associated with research concentrating on the innovation and use of hybrid heat treatment for eutectoid steel powder (0.8 wt%) reinforced Al-Zn-Mg (Al 7075) alloy composites. Due to high hardness, wear resistance, tensile strength and flexibility modifying heat treatment, heat treatable aluminium metal matrix composites reinforced with heat treatable hard steel particles may be the choice to explore. In this work, an attempt is made to increase hardness and tensile properties to higher levels through hybrid heat treatment, comprising simultaneous treatment to matrix and reinforcement in 3 different routes (Pearlite, Bainite and Martensite) compared to conventional age hardening treatment. SEM images and microhardness distribution witnessed the phase transformation in both matrix and reinforcement. Aging kinetics in conventional age hardening and hybrid treatments is accelerated by the increase in the quantity of reinforcement and increase in aging temperature. The improvement in hardness and tensile strength obtained by conventional age hardening path is further improved by the hybridisation path. Hybridisation route with martensite reinforcement phase shows excellent result in hardness, strength followed by bainite and pearlite path respectively in the decreasing order. In all heat treatment cycles, lower aging temperature marks greater property enhancement compared to higher temperature. Al 7075 with 6 wt% steel powder reinforced (martensite form) composite showed excellent peak age hardness, tensile strength compared to lesser quantity reinforced composites.